Mayer Rod

Interstitial wire-wound, film thickness 194.3 μm, diameter 9.52 mm, suitable for high viscosity fluid scraping.

Wire-wound, wet film thickness 105.2μm, diameter 9.52mm, Total length 400mm, Spreader width 300mm, material stainless steel, Wire diameter 1.17mm.

Production process is formed, wet film thickness 100.6 μm, diameter 9.52mm, Total length 400mm, Spreader width 300mm, material stainless steel.

Winding process, Wire diameter 0.13mm, rod diameter 12.7mm, the main rod and steel wire are stainless steel, can film 11.4μm.

The production process is formed, the wet film thickness is 20μm, the diameter is 10mm, the Total length is 400mm, the application width is 300mm, and the grip width is 50 + 50mm.

Stainless steel wire-wound Mayer Applicator rod, Wire diameter 0.53mm, scrapable wet film thickness 48.0μm, diameter 9.52mm, Total length 400mm, Spreader width 300mm

Also known as glue rod, using winding process, Wire diameter 0.30mm, rod diameter 12.7mm, the main rod and steel wire are stainless steel, RDS 12 #scraping rod can film 27.4μm.

Applicator rod adopts winding process, Wire diameter 0.46mm, rod diameter 6.35mm, main rod and steel wire are stainless steel, can film 41.1μm.

300Mm application width, 50μm film WFT, rod diameter is 10mm, can be manually or automatically scraped, hand width 50 + 50mm, material 304 stainless steel.

No. 5 Applicator rod is a formed Spreader process, which has the advantage of easy cleaning of continuous wire. Spreader wet film thickness is 5μm, and the effective application width is 300mm.

Wire-wound, wet film thickness 100μm, diameter 9mm, Total length 375mm, application width 255mm, hand width 60mm, material stainless steel.

Formed Coating Applicator, cleaning simple continuous wire, film thickness of 18 microns, effective application width of 300mm, 50mm at both ends, no need for a handle.

Applicator rod adopts winding process, Wire diameter 0.51mm, rod diameter 6.35mm, main rod and steel wire are stainless steel, 20 #Wire-wound drawdown Bar can film 45.7μm.

Using wire-wound process, stainless steel film scraping rod, rod diameter is 9.5mm, wire-wound Wire diameter is 1.32mm, preparatory film of 118.9μm.

Mayer Rods imported from the United States, formed process, suitable for levelling, sagging, color matching, color repair, hiding power, fingerprint resistance, etc. Film thickness is 205.7 μm, manual scraping, uniform film.

Formed process Mayer Rods, rod diameter 6.35mm, can be prepared 20.6 μm wet-film, easier to clean than wire-wound Applicator rod, continuous wire.

Applicator rod adopts winding process, Wire diameter 0.56mm, rod diameter 6.35mm, main rod and steel wire are stainless steel, can film 50.3μm.

Wet film thickness 200μm, application width 300mm, formed process, continuous wire easy to clean, wear-resistant anti-corrosion stainless steel material, suitable for Coating, coating, glue or Miscellaneous materials need a specific thickness of the film sample.

6 micron Coating thickness high-precision prepative, application width 300mm, widely used in pulp and paper, Spinning & weaving, Coating, Leather, Optical inspection film, Encasement materials and polymer materials and other precise quantitative preparatory film laminating experiments.

Wire-wound, wet film thickness 25.1μm, diameter 12.7mm, Total length 400mm, Spreader width 300mm, material stainless steel, Wire diameter 0.28mm.

Smooth steel bar with a diameter of 6.35mm, commonly used for Spreader pre-dosing on paper, Cardboard or Plastic film.

No. 9 RDS wire rod Film thickness 20.6 μm, rod diameter 6.35mm, Spreader width 300mm, hand width 50 + 50mm, 304 stainless steel material, Wire diameter 0.23mm.

Wire-wound, wet film thickness 24μm, diameter 9mm, Total length 375mm, application width 255mm, hand width 60mm, material stainless steel.

Using formed molding technology, the rod diameter is 6.35mm, the film can be 13.7μm, the application width is 300mm, and it has the characteristics of continuous wire and easy cleaning.