LENETA WC-55 Film Applicator film thickness 106µm

LENETAWC-55 Lacquer Film Applicator Wire diameter 1.40mm, WC-55 Lacquer Film Applicator is made of all stainless steel

Brand

SKU: NB010387

LENETA

Model

WC-55

Get Quote

LENETA shop

Information

Datasheet

What else did others buy

Genuinegoods

LENETA WC-55 Mayer RodsOverview
Specifications
Comments
FAQs

WC-55

Mayer Rods

Wire bar applicator

The coating is prepared into a film of a certain thickness, also known as a wire rod applicator, Meyer rod, and winding rod.

Features

Wire Diameter: 0.064~1.9mm(2.5~75mils)

Prepared coating film thickness: 4.5~150μm (0.18~6mils)

Coating Width: 254mm (10inches) long enough to meet most standard size baseplates and cardboards.

Bar length: 305mm (12inches). There are 25mm long grip parts at each end.

Bar diameter: 12.7mm (1/2inch). Thick enough to provide basic good rigidity.

Material: All stainless steel. Even water-based paints do not rust or corrode. Non-magnetic, allowing for use with steel plates on magnetic cards.

Parameters

Model	Wire diameter	Coating film thickness	Coating width
WC-2.5	0.064mm(2.5mil)	4.5µm(0.18 mil)	254mm(10 in)
WC-3	0.075mm(3mil)	5µm(0.2 mil)	254mm(10 in)
WC-4	0.10mm(4mil)	8µm(0.3 mil)	254mm(10 in)
WC-6	0.15mm(6mil)	10µm(0.4 mil)	254mm(10 in)
WC-8	0.20mm(8mil)	13µm(0.5 mil)	254mm(10 in)
WC-10	0.25mm(10mil)	16µm(0.65 mil)	254mm(10 in)
WC-12	0.30mm(12mil)	20µm(0.8 mil)	254mm(10 in)
WC-14	0.36mm(14mil)	24µm(0.95 mil)	254mm(10 in)
WC-16	0.41mm(16mil)	28µm(1.1 mil)	254mm(10 in)
WC-18	0.46mm(18mil)	32µm(1.25 mil)	254mm(10 in)
WC-20	0.51mm(20mil)	35µm(1.4 mil)	254mm(10 in)
WC-22	0.56mm(22mil)	38µm(1.5 mil)	254mm(10 in)
WC-24	0.61mm(24mil)	42µm(1.7 mil)	254mm(10 in)
WC-26	0.66mm(26mil)	47µm( 1.8mil)	254mm(10 in)
WC-28	0.71mm(28mil)	50µm(2.0 mil)	254mm(10 in)
WC-30	0.76mm(30mil)	55µm(2.2 mil)	254mm(10 in)
WC-32	0.81mm(32mil)	59µm(2.3 mil)	254mm(10 in)
WC-34	0.86mm(34mil)	63µm(2.5 mil)	254mm(10 in)
WC-36	0.91mm(36mil)	68µm(2.7 mil)	254mm(10 in)
WC-38	0.97mm(38mil)	72µm(2.8 mil)	254mm(10 in)
WC-40	1.02mm(40mil)	75µm(3.0 mil)	254mm(10 in)
WC-42	1.07mm(42mil)	81µm(3.2 mil)	254mm(10 in)
WC-44	1.12mm(44mil)	85µm(3.3 mil)	254mm(10 in)
WC-46	1.17mm(46mil)	89µm(3.5 mil)	254mm(10 in)
WC-48	1.22mm(48mil)	93µm(3.7 mil)	254mm(10 in)
WC-50	1.27mm(50mil)	98µm(3.8 mil)	254mm(10 in)
WC-52	1.32mm(52mil)	100µm(4.0 mil)	254mm(10 in)
WC-55	1.40mm(55mil)	106µm(4.2 mil)	254mm(10 in)
WC-60	1.52mm(60mil)	114µm(4.5 mil)	254mm(10 in)
WC-65	1.65mm(65mil)	125µm(5.0 mil)	254mm(10 in)
WC-70	1.78mm(70mil)	138µm(5.5 mil)	254mm(10 in)
WC-75	1.91mm(75mil)	150µm(6.0 mil)	254mm(10 in)
WC-212	N/A	N/A	254mm(10 in)

Optional

LENETA WC-55 Mayer RodsSpecifications

LIST	VALUE
Production process	Wire-wound
WFT	106µm
diameter	12.7mm
Total length	305mm
Wire diameter	1.40mm
Application width	254mm
grip width	25+25mm
material	stainless steel

LENETA WC-55 Mayer Rods Packing list

Coating applicator X1

[Note] Because the manufacturer's packaging may be updated or upgraded, the detailed packaging list shall be subject to the latest standard configuration of the manufacturer.

FAQ

[Q]

Meet JB/T5946 Mayer Rods

[A]

WC-55 Mayer Rods, please refer to it.

[Q]

Can silicone coatings be applied to quartz Glass substrates?

[A]

Yes, choose quartz Glass as the substrate, with Mayer Rods Coating prepared above coated on the surface of the treated quartz Glass substrate, at room temperature to evaporate the solvent into the oven, at a certain temperature curing film formation.

[Q]

Solid content of the sample is 32% and Dry-Film is 34 microns. Do you have any suggestions?

[A]

This one is fine.