LEEB Type C Hardness Gauge Impact unit for steel and cast/alloy tool steels
The LEEB Type C Impact Device is an Optional accessory to the LEEB 120 and LEEB 140 Leeb Hardness Testers for the measurement of steel and cast/alloy tool steel materials.
Leeb
-
Metal Leeb Hardness Tester KAIRDA NDT290 + Hardness measurement of various metal materials
Login -
KAIRDA NDT280 + Portable Leeb Hardness Tester metal shell color screen
$ 314.00 -
LEEB DL Hardness Gauge Impact unit for steel and cast steel materials
Login -
IPRE G Impact device for measurement of large and heavy specimens and castings and forgings with rough surfaces
$ 353.00 -
Deguang Electronics G-type Leeb Hardness Tester for measurement of large or heavy specimens and castings and forgings with coarse surfaces
$ 1105.00
product description
Leeb C-type impact device is an optional accessory for Leeb120 and Leeb140 Leeb Hardness Testers for measuring steel and cast steel/alloy tool steel materials.
Product testing range
| Material | Hardness system | Impact device | |||
| D/DC | C | G | DL | ||
| steel and cast steel | HRC | 17.1～68.5 | 20.0～69.5 | 20.6～68.2 | |
| HRB | 59.6～99.6 | 47.7～99.9 | 37.0～99.9 | ||
| HB | 140～651 | 80～683 | 90～646 | 150～646 | |
| HV | 83～976 | 80～996 | 85～950 | ||
| HS | 26.4～99.5 | 31.9～102.3 | 26.5～99.4 | ||
| forged steel | HB | 142～651 | |||
| alloy tool steel | HRC | 17.1～67.1 | 20.0～69.5 | ||
| HV | 83～976 | 80～996 | |||
| Stainless steel | HRB | 59.6～99.6 | |||
| HB | 140～651 | ||||
| HV | 83～976 | ||||
| grey cast iron | 140～334 | 92～326 | |||
| Ductile Iron | HB | 140～387 | 140～364 | ||
| cast aluminum alloy | HB | 30～159 | |||
| copper zinc alloy | HB | 40～173 | |||
| Copper-tin alloy (bronze) | HB | 60～290 | |||
| pure copper | HB | 45～315 | |||
Pictures
Leeb Type C Impact device (Hardness Gauge)Specifications
| LIST | VALUE |
|---|---|
| Impact energy | 2.7mJ |
| Impact device Mass | 3.0g |
| Ball Hardness | 1600HV |
| Ball head diameter | Ball head material |
| Ball head material | tungsten carbide |
| Impact device diameter | 20mm |
| Impact device length | 141mm |
| Impact device Mass | 75g |
| Maximum Specimen Hardness | 1000HV |
| Specimen Surface Roughness | 0.4µm |
| Minimum specimen Weight | >1.5kg |
| Need stable support | 0.5~1.5kg |
| Dense coupling is required | 0.02~0.5kg |
| Minimum test Film thickness | 1mm |
| Minimum depth of hardened layer | ≥0.2mm |
| Hardness 300HV Indentation Diameter | 0.38mm |
| Hardness 300HV Indentation | 12µm |
| Hardness 600HV Indentation Diameter | 0.32mm |
| Hardness 600HV Indentation | 8µm |
| Hardness 800HV Indentation Diameter | 0.35mm |
| Hardness 800HV Indentation | 7μm |
| Application of impact device | C-type impact force is small, the surface damage is small, does not destroy the hardened layer, suitable for measurement of small thin parts and surface hardened layer. |
Leeb Type C Impact device (Hardness Gauge) Packing list
Impact device x1, Certificate x1, Manual x1, Encasement box x1
[Note] Because the manufacturer's packaging may be updated or upgraded, the detailed packaging list shall be subject to the latest standard configuration of the manufacturer.
FAQ
- ActiveDL/T 1845-2018
- ActiveGB/T 13313-2008
- ActiveGB/T 17394.1-2014
- ActiveGB/T 17394.4-2014
- ActiveGB/T 17394.3-2022
- ActiveGB/T 17394.2-2022
- AbolishGB/T 17394-1998
- AbolishGB/T 17394.3-2012
- AbolishGB/T 17394.2-2012
- ActiveJB/T 9378-2001