Mayer Rod

The popular rod number of RDS, the application involves dozens of sub-segments, such as silver-coated nanowires, polymer nano-films. 13.7 micron wet film thickness, this model is wire-wound steel rod, 3/8 inch main rod diameter.

Mainstream models of inks scraping samples, Mayer wire-wound principle, Wire diameter 0.13mm, about 11 micron wet-film control, suitable for the application of Wire-wound drawdown Bar inspection on inks Color tinctorial strength in the newly released GB/T13217.1 standard in 2020.

Wire-wound, wet film thickness 12μm, diameter 3mm, Total length 245mm, application width 140mm, grip width 60mm, material stainless steel. One-handed film

Wire-wound, wet film thickness 18.3μm, diameter 9.52mm, Total length 400mm, Spreader width 300mm, material stainless steel, Wire diameter 0.20mm.

Formed Spreader process, wet film thickness 17μm, film accuracy 0.5μm, fine workmanship, high-quality stainless steel material, can be purchased separately handle matching use.

Can film 13.7 μ m, using winding process, Wire diameter 0.15mm, rod diameter 6.35mm, the main rod and steel wire are stainless steel.

Winding process, Wire diameter 0.13mm, rod diameter 6.35mm, the main rod and steel wire are stainless steel, can film 11.4μm.

Wire-wound Mayer Rods, 1/4 inch (6.35mm) in diameter, 400mm in Total length, 300mm in effective Spreader width, made of wear-resistant stainless steel.

Can film 11.4 μm, formed molding technology, rod diameter of 6.35mm, with continuous wire, easy to clean and so on.

It is suitable for preparing 18.3μm wet-film, rod diameter 6.35mm, Total length 400mm, effective Spreader width 300mm, suitable for Coating inks, Resin, Plastic, Pressure sensitive adhesive, etc.

The production process is formed, the wet film thickness is 20μm, the diameter is 10mm, the Total length is 250mm, the application width is 250mm, and the grip width is 0 + 0mm.

The production process is formed, wet film thickness 11.4 μm, diameter 9.5mm, Total length 400mm, Spreader width 300mm, material stainless steel.

Applicator rod adopts winding process, Wire diameter 0.18mm, rod diameter 6.35mm, main rod and steel wire are stainless steel, can film 16.0μm.

Popular RDS rod number, wet film thickness 13.7μm, production process formed, diameter 9.52mm, Total length 400mm, Spreader width 300mm, material stainless steel.

Formed molding technology, rod diameter 6.35mm, Film thickness 16.0μm, Spreader width 300mm, with continuous wire, easy to clean and other characteristics.

The production process is formed, the wet film thickness is 16.0μm, the diameter is 9.52mm, the Total length is 400mm, the Spreader width is 300mm, and the material is stainless steel.

Formed applicator rod, film thickness of 18 microns, for experimental prepative film, application width of 250mm, no hand grip part, can be equipped with handle Spreader more easily.

The production process is formed, the wet film thickness is 12μm, the diameter is 10mm, the Total length is 250mm, the application width is 250mm, the grip width is 0, and the material is 304 stainless steel.

The production process is formed, the wet film thickness is 13μm, the diameter is 10mm, the Total length is 250mm, the application width is 250mm, the grip width is 0, and the material is 304 stainless steel.

The production process is formed, the wet film thickness is 22μm, the diameter is 10mm, the Total length is 250mm, the application width is 250mm, the grip width is 0, and the material is 304 stainless steel.